Superwool Blok Plus

Superwool Blok Plus

Superwool Blok Plus boards are made of mineral fibres and a small amount of organic binder. As a result of the high fibre content, Superwool Blok Plus boards are strong, lightweight and resistant to thermal shocks. All grades of Superwool Blok Plus are hydrophobically impregnated to prevent the absorption of water or concrete binders.

Classification temperature:
Superwool Plus Blok 800 800°C
Superwool Plus Blok 1000 1000°C
Superwool Plus Blok 1100 1100°C
Superwool Plus Blok 1100 LQ 1100°C
Superwool Plus Blok AL 1000°C

  •  

    Superwool Plus Blok 800 Superwool Plus Blok 1000 Superwool Plus Blok 1100 Superwool Plus Blok 1100 Superwool Plus Blok AL
    Colour white / oak
    Classification temperature °C 800 1000 1100 1100 1000
    Density kg/m3 320 320 320 320 320
    Modules of rupture, MPa *unfired 0,7 0,8 0,8 0,9 0,8
    Compressive strength, MPa 10% relative deformation 0,3 0,3 0,3 0,3 0,3
    Water absorption after 2 hours, % 5,5 5,0 5,0 5,0 5,5
    Thermal conductivity, (W / m)
    200°C 0,05 0,06 0,05 0,05 0,5
    300°C 0,05 0,06 0,06 0,06 –
    400°C 0,06 0,07 0,07 0,07 0,7
    500°C 0,07 0,09 0,08 0,08 –
    600°C 0,08 0,1 0,09 0,09 0,1
    800°C 0,12 0,13 0,12 0,12 0,13
    900°C – – – – 0,14
    1000°C – – 0,16 0,16 –
    Loss of ignition after 2 hours
    1000°C 1,4 – – – 2,0
    1100°C – 1,4 1,3 1,3 –
    Chemical composition (%)
    Al2O3 13,9 15,1 10,1 16,2 18,7
    SiO2 61,2 59,4 59,5 56,5 54
    CaO + MgO 18,3 19,4 28,2 24,6 20,9
    Fe2O3 + TiO2 3 3,8 1,2 1,3 4,7
    Na2O+K2O 3,6 2,3 1 1,4 2,4

  •  

    Superwool Plus Blok 800 Superwool Plus Blok 1000 Superwool Plus Blok 1100 Superwool Plus Blok 1100 Superwool Plus Blok AL
    Thickness (mm) 25, 30, 40, 50, 60, 70, 80, 90, 100
    Standard size (mm) 1000 x 1200,  1000 x 600